One-step synthesis route of the aligned and non-aligned single crystalline α-Si3N4 nanowires

TLDR: In this paper, the authors reported the bulk synthesis route of the aligned and non-aligned high-quality α-Si3N4 nanowires (NWS) which were grown directly from the Si substrate by vapor phase deposition at 1050°.

Abstract: This paper reports the bulk synthesis route of the aligned and non-aligned high-quality α-Si3N4 nanowires (NWS) which were grown directly from the Si substrate by vapor phase deposition at 1050° The as-grown products were characterized by employing XRD, SEM, HRTEM and photoluminescence The microscopic results revealed that the products consist of single crystalline aligned and non-aligned α-Si3N4 NWs having a same diameter range of 30–100 nm and different lengths of about hundreds of microns The XRD observation revealed that the products consist of α-phase Si3N4 NWs The room temperature PL spectra indicated that the NWs have good emission property The non-aligned NWs were formed at lower temperature as compared with aligned NWs Our method is a simple and one-step procedure to synthesize the bulk-quantity and high-purity aligned and non-aligned α-Si3N4 NWs at a relatively low temperature The possible growth mechanism was also briefly discussed