About: National Institute of Advanced Industrial Science and Technology is a government organization based out in Tsukuba, Ibaraki, Japan. It is known for research contribution in the topics: Catalysis & Thin film. The organization has 22114 authors who have published 65856 publications receiving 1669827 citations. The organization is also known as: Sangyō Gijutsu Sōgō Kenkyū-sho.

Copper-catalyzed aerobic oxidative coupling of terminal alkynes with H-phosphonates leading to alkynylphosphonates.

Abstract: Copper catalyzed the aerobic oxidative coupling of terminal alkynes with H-phosphonates to afford alkynylphosphonates in high yields.

Synthesis of Porous Silicon Nitride with Unidirectionally Aligned Channels Using Freeze-Drying Process

Abstract: Porous silicon nitride with macroscopically aligned channels was synthesized using a freeze-drying process. Freezing of a water-based slurry of silicon nitride was done while unidirectionally controlling the growth direction of the ice. Pores were generated subsequently by sublimation of the columnar ice during freeze-drying. By sintering this green body, a porous silicon nitride with high porosity (over 50%) was obtained and its porosity was controllable by the slurry concentration. The porous Si 3 N 4 had a unique microstructure, where macroscopically aligned open pores contained fibrous grains protruding from the internal walls of the Si 3 N 4 matrix. It is hypothesized that vapor/solid phase reactions were important to the formation mechanism of the fibrous grains.

Processing and mechanical properties of autogenous titanium implant materials

Abstract: Pure titanium and some of its alloys are currently considered as the most attractive metallic materials for biomedical applications due to their excellent mechanical properties, corrosion resistance, and biocompatibility. It has been demonstrated that titanium and titanium alloys are well accepted by human tissues as compared to other metals such as SUS316L stainless steel and Co–Cr–Mo type alloy. In the present study, highly porous titanium foams with porosities ≤80% are produced by using a novel powder metallurgical process, which includes the adding of the selected spacers into the starting powders. The optimal process parameters are investigated. The porous titanium foams are characterized by using optical microscopy and scanning electron microscopy. The distribution of the pore size is measured by quantitative image analyses. The mechanical properties are investigated by compressive tests. This open-cellular titanium foams, with the pore size of 200–500 μm are expected to be a very promising biomaterial candidates for bone implants because its porous structure permits the ingrowths of new-bone tissues and the transport of body fluids.